Gold adhesion to Ti oxide
2009-06-19
mikas remeika
2009-06-20
ning xue
2009-06-20
Alex Mellnik
2009-06-21
Xiaoguang Liu
2009-06-21
mikas remeika
2009-06-21
Prasanna Srinivasan
2009-06-21
Pavan Samudrala
2009-06-21
Kagan Topalli
2009-06-22
Morrison, Richard H., Jr.
2009-06-22
shimul saha
2009-06-22
abhaya joshi
2009-06-22
Albert Henning
Gold adhesion to Ti oxide
ning xue
2009-06-20
Maybe you can try Cr-AU E-beam




2009/6/19 mikas remeika 

> Hello,
>
> does anybody have experience dealing with this kind of issue:
>
> I'm trying to deposit a film of gold on top of a thin film of titanium
> (e-beam evaporated), the titanium is exposed to air (and oxygen plasma)
> during previous processing, so its inevitable that there is a thin layer of
> oxide on the surface of the titanium.
>
> A Gold film is e-beam evaporated onto the surface of the Ti (TiO2).
> Resulting film adheres well enough to perform lift-off, however, mechanical
> stress such as wireboding results in large sections of the gold film
> peeling
> off.  I have tried evaporating a fresh layer of Ti under the gold (in the
> same vacuum), that did not give any improvement in adhesion.  I also have
> access to sputtering machines, however in previous experience evaporated
> gold adhered more reliably to different surfaces.
>
> So my question - is there are way to treat the titanium/TiO2 surface to
> create good adhesion to the gold layer? I have acceess to a range of
> materials for sputtering and evaporation, if there is a specific material
> that adheres well to both gold and TiO2 I would really like to know what it
> is.
>
> Some notes: The sample in this case cannot be heated to more than 100C and
> cannot be exposed to RIE type plasma.  Also, it is necessary to have
> electrical contact between the gold and titanium (the naturally formed
> oxide
> in this case does not create electrical insulation).
>
> Thank you very much for any advice,
>
> -Mikas
> _______________________________________________
> Hosted by the MEMS and Nanotechnology Exchange, the country's leading
> provider of MEMS and Nanotechnology design and fabrication services.
> Visit us at http://www.mems-exchange.org
>
> Want to advertise to this community?  See http://www.memsnet.org
>
> To unsubscribe:
> http://mail.mems-exchange.org/mailman/listinfo/mems-talk
>
reply
Events
Glossary
Materials
Links
MEMS-talk
Terms of Use | Contact Us | Search
MEMS Exchange
MEMS Industry Group
Coventor
Harrick Plasma
Tanner EDA
Tanner EDA by Mentor Graphics
University Wafer
MEMS Technology Review
Mentor Graphics Corporation