MEMSnet Home: MEMS-Talk: make the su-8 surface flat
make the su-8 surface flat
2011-06-10
첸로
2011-06-10
Khaled Mohamed Ramadan
2011-06-10
Xiaohui Lin
2011-06-10
첸로
2011-06-10
Eric Johnston
2011-06-11
첸로
2011-06-11
dai truong
2011-06-12
gau s
2011-06-13
Shane GUO
2011-06-14
Khaled Mohamed Ramadan
2011-06-14
Shane GUO
2011-06-15
Gareth Jenkins
2011-06-15
Shane GUO
2011-06-16
첸로
2011-07-06
Le Hong Hanh
2011-07-12
Shane GUO
2011-07-16
Bill Moffat
make the su-8 surface flat
Shane GUO
2011-07-12
Hi all,

Gareth is correct. Dehydration is very important for my case. Because my last
wafer has another polymer layer beneath the SU-8 layer, I cannot bake the
substrate above 90C for dehydration. By using a clean wafer, baked at 200C for
15mins and treated by O2 plasma for 10mins, I spin coated SU-8(50) at 1500rpm
for a 80um thick film. The coated wafer was relaxed overnight and no pulling
back was observed. Surface was very flat (visually) as expected except for the
edge bead (around ~5mm wide for a 4inch wafer). I did not remove the edge bead
and it had no influence on me, since my feature size is relatively large.

Thank you all
reply
Events
Glossary
Materials
Links
MEMS-talk
Terms of Use | Contact Us | Search
MEMS Exchange
MEMS Industry Group
Coventor
Harrick Plasma
Tanner EDA
MEMS Technology Review
Nano-Master, Inc.
Addison Engineering
The Branford Group