3000A Cr by thermal evaporation?
2002-04-09
Soojin Oh
2002-04-10
Richard Morrison
2002-04-09
Henry Yang
3000A Cr by thermal evaporation?
Richard Morrison
2002-04-10
Hi,

Cr depositions are usually high stress, I would think that at 3000A the
stress was very high, did you measure the stress?


How did you clean the wafers? they are never clean when you get them
from the supplier, usually you do a version of the RCA clean before
deposition.

Rick


Soojin Oh wrote:

>3000A Cr was deposited by thermal evaporation on top
>of SiO2 surface, and kept on table top for 3 month. Cr
>layer peels off when DI water is squirted onto the
>surface from wherever water touches. Can you suggest
>any possible causes? Contact surface was supposedly
>clean because I handed new clean wafers to this person
>who did evaporation, but I don't know what kind of
>effort was made to clean them further. Cr layer was ok
>right after deposition, 3 month ago.
>Thank you.
>
>-Soojin
>Yahoo! Tax Center - online filing with TurboTax
>http://taxes.yahoo.com/
>_______________________________________________
>[email protected] mailing list: to unsubscribe or change your list
>options, visit http://mail.mems-exchange.org/mailman/listinfo/mems-talk
>Hosted by the MEMS Exchange, providers of MEMS processing services.
>Visit us at http://www.mems-exchange.org/

reply
Events
Glossary
Materials
Links
MEMS-talk
Terms of Use | Contact Us | Search
MEMS Exchange
MEMS Industry Group
Coventor
Harrick Plasma
Tanner EDA
MEMS Technology Review
The Branford Group
Mentor Graphics Corporation
Tanner EDA by Mentor Graphics